■ Characteristic
BC-4HR is polypropylene grafted with maleic anhydride, which is a kind of adhesive polypropylene resin especial for STEEL/PPR composite pipe. BC-4HR keeps good processing and mechanical performance of polypropylene, at the same time, it also has excellent cohesive property and can bond firmly to polypropylene (PPR) and metals such as aluminum, steel, copper, etc.
Typical Property Data of BC-4HR
Property | Unit | Test Method | Spec. Value |
Appearance |
|
| white equal pellets |
Melt Flow Rate | g/10min | GB/T3682 | 2～6 |
Density | g/cm3 | GB/T1033 | >0.9 |
Tensile Strength at Break | MPa | GB/T1042 | ＞19 |
Elongation at Break | ％ | GB/T1040 | ＞400 |
Vicat Softening Point | ℃ | GB/T1633 | ＞105 |
Melting Point | ℃ | GB/T4608 | 155 |
■ Application
It is adhesive resin especial for STEEL/PPR composite pipe and is suitable for co-extrusion or coating processing. Suggested extrusion temperature from feeding zone to die: 160℃, 180℃, 200℃, 220℃-230℃.
Adhesive property of BC-4HR with different base material
Material | Thickness(mm) | Adhesive Strength(N/25mm) |
Aluminum | 0.2 | >100 |
Steel | 1.0 | >140 |
Copper | 0.2 | >80 |
■ Package, storage and transportation:
Packed in paper plastic composite bags, 25kg/bag.
Keep away from sun light, rain and wet
Note: The technical data contained herein is believed to be reliable, but users should not rely upon it absolutely for specific applications because performance properties will vary with processing conditions. Users of PARKSON products should make their own tests to determine the suitability of each such product for their particular purposes. Above is the typical experimental data, real and reliable. It is only used for reference, not as formal quality promise.