MAH-G-copolymerization polypropylene （AD-105）

Characteristic:

AD-105 is maleic anhydride graft copolymerization polypropylene, which is used to fill or reinforce polypropylene. As a polymer coupling agent, it can greatly improve the mechanical and thermal properties of filled or reinforced polypropylene. A polar group is introduced into the polypropylene molecular chain, so that the coloring capability of the polypropylene is remarkably improved.  

                                    AD-105 Typical Property Data

Performance

Index

Appearance

White or light yellow equal pellets

Maleic anhydride content %

1.0-1.4

Melt Flow Rate（g/10min）

5-15（190℃/0.325）

Matrix resin

Block
copolymer
of
propylene


Application: AD-105 is mainly used for filling or strengthening polar materials.As a modified agent for fiber reinforced PP, filling PP (talcum powder, calcium carbonate, aluminum hydroxide, magnesium hydroxide, wood powder, mica and wollastonite ); the addition amount is 2.5% -10% (relative to PP).


                   30% Glass Fiber Reinforced PP Performance

Addition amount（AD-105）

Tensile Strength at Break (MPa)

bending strength (MPa)

Notched impact strength (kJ/m2)

Heat
distortion
temperature

(1.82MPa) ℃

0%

35

45

5

125

2.5%

65

90

10

135

5%

75

120

12

145


Method of use: blended with PP


Packed in paper plastic composite bags, 25kg/bag. Keep away from sun light, rain and wet.

The technical data contained herein is believed to be reliable, but users should not rely upon it absolutely for specific applications because performance properties will vary with processing conditions. Users of BAICHEN products should make their own tests to determine the suitability of each such product for their particular purposes. Above is the typical experimental data, real and reliable. It is only used for reference, not as formal quality promise.